Metal-to-moat contacts in N-channel silicon gate integrated circuits using discrete second-level polycrystalline silicon

ABSTRACT

A double-level polycrystalline silicon structure for an N-channel MOS integrated circuit is disclosed including a metal interconnect level. Contact between the metal interconnect level and N+ diffused moat areas is made through discrete second-level polysilicon areas which reduce the step from metal level to moat level, thus increasing yields. Also, connections from the metal level to the first level polysilicon are made using a discrete area of second level polysilicon to minimize the step.

BACKGROUND OF THE INVENTION

This invention relates to semiconductor devices and methods of manufacture thereof, and more particularly to an improved contact and interconnect arrangement for N-channel, silicon-gate MOS integrated circuits of the type having double-level polycrystalline silicon structures.

MOS integrated circuits employing double-level polysilicon processes are disclosed in prior pending applications as follows, all assigned to Texas Instruments:

Ser. No. 648,594, filed Jan. 12, 1976 by C-K Kuo

Ser. No. 722,841, filed Sept. 13, 1976 by C-K Kuo

Ser. No. 754,144, filed Dec. 27, 1976 by L. S. Wall

Ser. No. 762,613, filed Jan. 26, 1977 by D. J. McElroy

In addition, a double-level poly structure is shown in Electronics, Feb. 19, 1976, pp. 116-121.

The prior semiconductor manufacturing methods have used second-level polycrystalline silicon with its underlying gate oxide as a diffusion mask to create the N+ diffused regions in N-channel, silicon-gate MOS devices. This has limited the utility of the various levels as interconnects, and contacts between the levels has been restricted. Supposedly, in a double-level poly structure, there are four interconnect levels: N+ moat; first level poly; second level poly; metallization. However, with prior methods, the second level poly could not cross an N+ moat region as it was the diffusion mask, i.e., created a transistor when it crossed a moat. Also, metal to moat contacts were not readily made due to the step caused by the thicknesses of the several layers and the interleaved insulators.

It is therefore the principal object of the invention to provide an improved N-channel silicon-gate semiconductor device and method of manufacture. Another object is to provide an improved contact and interconnect arrangement for integrated circuits.

SUMMARY OF THE INVENTION

In accordance with an embodiment of the invention, a double-level polycrystalline silicon integrated circuit structure is shown which includes a metal interconnect level as well as heavily-doped moat regions, all of which can provide contacts and interconnections. Contacts between the metallization level and moat areas is made through discrete second-level polycrystalline silicon areas which function to reduce the step from metal level to moat level which would result from the thicknesses of the several levels. Likewise, contact between metallization level and the first level polysilicon is made through a discrete area of second level poly which functions to reduce the step.

BRIEF DESCRIPTION OF THE DRAWINGS

The novel features believed characteristic of the invention are set forth in the appended claims. The invention itself, however, as well as other features and advantages thereof, will be best understood by reference to the detailed description which follows, read in conjunction with the accompanying drawings, wherein:

FIG. 1 is a greatly enlarged plan view of a small portion of a semiconductor chip showing the physical layout of a static RAM cell using the features of the invention;

FIG. 2 is an electrical schematic diagram of the cell of FIG. 1;

FIGS. 3a-3d are elevation views in section of the cell of FIG. 1, taken along the lines a--a, b--b, c--c and d--d, respectively;

FIGS. 4a-4d are elevation views in section of the semiconductor device of FIGS. 1 and 3a, at successive states in the manufacturing process, taken along the line a--a in FIG. 1; and

FIG. 5 is a plan view of a layout of the cell of FIG. 1 in an array.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENT

Referring to FIG. 1, a physical layout is shown of an N-channel silicon gate MOS static RAM cell which utilizes the features of the invention. This cell is of course greatly enlarged in FIG. 1, as it would actually occupy only about 1.5 to 2.0 square mils, i.e., the larger dimension of the cell of FIG. 1 would be less than about two mils. The cell is also shown in FIG. 2 as an electrical schematic diagram, with the parts numbered the same as FIG. 1.

The cells of FIGS. 1 and 2 consists of a pair of cross-coupled driver transistors Q1 and Q2, each of which has a source 10 or 11 in the form of an N+ region connected to an elongated N+ diffused strip which is a ground or Vss line 12. Each transistor has an N+ drain region 13 or 14 which is electrically connected via nodes N1 and N2 to a Vcc or positive supply line 15 through a resistor R1 or R2. The resistors R1 and R2 are formed by ion implantation in a second-level polycrystalline silicon layer according to a feature of this embodiment of the invention. The Vcc supply line 15 is an elongated heavily doped region of the second-level poly. A node or contact area 16 at the drain 13 of the transistor Q2 is connected to a first level polysilicon strip which forms the gate 17 of the transistor Q1 and the node N2 in one polysilicon conductor 18. In like manner a first-level polysilicon conductor 20 connects the poly gate 21 of the transistor Q2 to the node N1 at the drain 14 of the transistor Q1, providing the cross-coupling connection of a bistable or flip-flop circuit. Metal strips which provide data lines 23 and 24 (usually referred to D and D, or as D0 and D1) are connected to the nodes N1 and N2 via coupling transistors Q3 and Q4 and metal-to-moat contacts 25 and 26 which include a second-level poly layer according to a feature of one embodiment. The gates 27 and 28 of the transistors Q3 and Q4 are connected to (actually part of) a word address line 29 which is a first-level polysilicon strip.

Referring to FIGS. 3a-3d, sectional views of the cell of FIG. 1 show the details of construction. The cell is a small part of a substrate 30 of P-type silicon. The transistors Q1, Q2, Q3 and Q4 are formed in elongated moat regions in which N+ diffused regions 10, 11, 12, 13 and 14 create the Vss line and source and drain regions for the transistors. Also, N+ regions 32 and 33 in the moats form the lower part of the metal-to-moat contacts 25 and 26. A thin silicon oxide gate dielectric layer 34 and phosphorus-doped first-level polysilicon areas 17, 18, 20, 21, 27, 28 and 29 form the gates of the transistors, the interconnects, and the address line. The polysilicon strips which form the gates 17 and 21 are parts of the elongated strips which include the cross-coupling interconnects. Thick field oxide 35 exists at all areas where moats including N+ diffused regions or transistors do not exist, and a P+ boron-doped channel-stop region 36 is created under all areas of the field oxide 35. An insulating layer 37 is formed over the entire top surface, overlying the polysilicon, the field oxide 39, and the N+ regions. The lines 23 and 24 are metal strips overlying this insulating layer 37.

As seen in FIGS. 3a, 3b and 3c, the resistors R1 and R2, according to a feature of this embodiment, consist of a phosphorus ion implanted portions of second-level polycrystalline silicon strips 38 and 39 which extend from the Vcc line 15. The remainder of the strips 38 and 39 as well as the line 15, except for the resistors R1 and R2, is heavily doped with phosphorus so that it will be highly conductive. The size of the resistor R1 or R2 is about 0.15 mil×0.3 mil in area as seen in plan view of FIG. 1, and about 5,000 A or 0.5 micron in thickness as seen in a section view as FIGS. 3a-3c. The resistor is seen to overly the first level poly line 20, and indeed overlies the gate 21 of the transistor Q1. This results in a savings in space on the chip which is quite significant. Also, the second level poly in which the resistors are formed does not form the gates of transistors, so it is less critical. The use of second-level poly further allows the Vcc line to overly the Vss line, which conserves additional space. The cell of FIGS. 1-3 is potentially about one-third the size of the static cell using implanted resistors in single level poly as disclosed in application Ser. No. 727,116.

An important feature is that the second level poly (or its underlying thin oxide) does not function as a diffusion mask; the first level poly is that which defines the extent of the N+ diffusions in the moats by means of the thin oxide 34 which is the diffusion mask. Therefore, the second level poly lines can cross over moats without creating transistors. In prior art double-level poly processes, such as shown in applications Ser. No. 648,594, filed Jan. 12, 1976 by C-K Kuo, or Ser. No. 754,144, filed Dec. 27, 1976 by L. S. Wall, the second-level poly is used to define the boundaries of the N+ diffusion, so that neither first nor second level is truly a versatile level of interconnections because these cannot cross over an N+ diffused moat. In the embodiment shown here, four levels of interconnects are available; the only constraint is that first level poly cannot cross an N+ moat.

As will be explained in detail in reference to the process for making the device of FIGS. 1-3, the thickness of the various layers are such that the step which would exist between the metallization level and the moat level is perhaps 10,000 to 15,000 A. This is inconsistent with acceptable yields. A step of this magnitude can produce discontinuities in the metal at the edges of a metal-to-moat contact. It is for this reason that a discrete area 40 of second-level polycrystalline silicon is positioned in the contact area 25 or 26 so that the step will be reduced by about 5000 A and yields increased. Heretofore, metal-to-moat contacts have been avoided, particularly in double-level poly structures.

The resistors R1 and R2 function as field-effect transistors because the resistance of these elements is dependent upon the voltage on the first level poly 18 and 20, i.e., the voltage on the nodes N1 and N2, assuming that the oxide layers 41 between first and second level poly is thin. This oxide may be about 3000 A in one example. The magnitude of each of the resistors R1 and R2 is about 500 K ohm or more when a "0" is stored on the corresponding node N1 and N2, but switches to about 30% or less of its higher value when a "1" is stored, assuming the "1" level to be +5 v. and the "0" level to be ground or Vss. This is in addition to the influence of the "source" voltage; the resistance will also change as a function of the voltage across it as explained in application Ser. No. 727,116. The more positive the voltage on the gate 21 in FIG. 3a, the lower the magnitude of the resistor R1. This functions to reduce power consumption in a large array of static cells; each cell will have one transistor on and one off, storing a "1" or "0," and the on transistor will have a high resistance in series with it to minimize power drain while the off transistor will have a low resistance in series so it will provide almost a full logic level voltage on the gate of the opposite transistor and almost a full logic level (minus a Vt drop for Q3 or Q4) to the output line 23 or 24 if the cell is addressed. The node N1 or N2 which is to be a "1" will charge to almost Vcc through the low resistance. Current dissipation, assuming the resistors R1 and R2 are 1 megohm, is 1 microamp per cell, or 16 milliamp for a 16 K array; power dissipation would be 80 milliwatts. Resistors R1 and R2 can be increased to values exceeding 20 megohm.

Referring now to FIGS. 4a-4e, a process for making the N-channel, silicon-gate, self-aligned, double-level poly, MOS integrated circuit device of FIGS. 1 and 3a-3d will be described. The starting material is a slice of P-type monocrystalline silicon, perhaps 3 inches in diameter and 20 mils thick, cut on the >100< plane, of a resistivity of about 6 to 8 ohm-cm. In FIGS. 3a or 4a, a wafer or body 30 represents a very small part of the slice, of about 1.5 mil in lateral dimension, chosen as a representative sample cross section. First, after appropriate cleaning, the slice is oxidized by exposing to oxygen in a furnace at an elevated temperature of perhaps 1000° C. to produce an oxide layer 41 of a thickness of about 1000 A. Next a layer 42 of silicon nitride Si₃ N₄ about 1000 A thick is formed by exposing to an atmosphere of silane and ammonia in an rf reactor. A coating 43 of photoresist is applied to the entire top surface, then exposed to ultraviolet light through a mask which defines the desired pattern, and developed, leaving areas 44 where nitride is to be etched away and field oxide 35 is to be grown. Alternatively, smaller geometrics and thus smaller cell sizes may be obtained by using electron beam lithography in place of uV light and glass masks to expose the photoresist, as disclosed in Bell Laboratories Record, March 1976, p. 69-72 and Electronic Products, February 1977, p. 17. The slice is subjected to a plasma etch, which removes the part of the nitride layer 42 not covered by the exposed photoresist 43, but does not remove the oxide layer 41 and does not react with the photoresist 43.

The slice is next subjected to an ion implant step, whereby boron atoms are implanted in the areas 44 of silicon not covered by phororesist 43 and nitride 42. The phororesist is left in place as an implant mask. Boron is an impurity which produces P-type conductivity, so more heavily doped P+ regions 45 will be produced in the surface. The oxide layer 41 is left in place during the implant because it prevents the implanted boron atoms from out-diffusing from the surface during subsequent heat treatment. The boron implant is at a dosage of about 4×10¹² /cm² at 100 KeV. After the implant, the photoresist layer 43 is removed.

As will be seen, the regions 45 do not exist in the same form in the finished device, because some of this part of the slice will have been consumed in the oxidation procedure. The implanted regions 45 will ultimately produce the P+ channel stop regions 36.

As set forth in patent application Ser. No. 684,593, filed Jan. 12, 1975 by G. R. Mohan Rao, assigned to Texan Instruments, the next step in the process is to subject the slice to a heat treatment or annealling step, during which the slice is maintained at a temperature of about 1000° C. for about 2 hours in an inert atmosphere, preferably nitrogen. This step causes the boron concentration to change markedly, which has desirable effects aside from reduction in bulk damage in the crystal structure. The P+ regions 45 penetrate deeper into the silicon surface during this anneal step.

The following step is formation of field oxide, which is done by subjecting the slices to steam or an oxidizing atmosphere at about 950° C. for perhaps 10 hours. As seen in FIG. 4b, this causes a thick field oxide region or layer 35 to be grown, and this region extends into the silicon surface because silicon is consumed as it oxidizes. The nitride layer 42 masks oxidation beneath it. The thickness of this layer 35 is about 8000 to 10,000 A, half of which is above the original surface and half below. The boron doped P+ region 45 as previously implanted and modified by the anneal step will be partly consumed, but will also diffuse further into the silicon ahead of the oxidation front. Thus, the P+ regions 36 will result which will be deeper and of more uniform and acceptable concentration at the surface compared to what would have resulted without the anneal step. Also, the regions 38 will not have the extent of crystalline structure damage characteristic of implanted devices.

The nitride layer 42 and its underlying oxide layer 41 are removed by etching, as the next step, and another thin silicon oxide layer 34 of about 800 A is grown over the exposed areas of silicon.

At this time, although not reflected in the FIGURES, two ion implant steps can be performed to create the desired threshold or operating parameters in transistors in the integrated circuit. First, boron is implanted in all moat areas at 50 KeV to a dosage of about 2.5×10¹¹ atoms per cm² for the purpose of adjusting the threshold voltage of thin oxide enhancement mode transistors so that substrate bias voltage will not be needed. Then, a photoresist layer is applied and patterned to expose the channel areas of depletion load transistors in peripheral circuitry, not in the cell array. These areas are then subjected to a phosphorus implant at 150 KeV with a dosage of about 1×10¹² per cm². This phosphorus implant is selected to produce high speed devices in the peripheral circuits. As explained in application Ser. No. 727,116, is depletion load transistors had been used in place of the resistors R1 and R2 in the cell array then attaining low standby power dissipation would have been the most important factor rather than speed in the peripheral circuits and so speed in terms of access time would be compromised. In addition, of course, the use of resistors R1 and R2 in second-level poly reduces the cell size.

Windows 46 for first level polysilicon to moat contacts are patterned and etched using photoresist removing the gate oxide layer 34 in selected areas such as the contact areas at the nodes N1 and N2. Next, a layer of polycrystalline silicon is deposited over the entire slice in a reactor using standard techniques, for example by decomposition of silane in hydrogen at about 930° C. to a thickness of 0.4 to 0.6 micron, producing the first-level polysilicon which is then patterned to form the strips 18 and 20, and the line 29, using photoresist. The resulting structure is seen in FIG. 4c. At the same time using the photoresist which patterns the first level poly, the thin oxide 34 is removed in all exposed areas, leaving oxide only in the transistor gate areas (plus capacitor areas, not shown, which may be needed in peripheral circuitry, as in boot-strap circuits).

Using the remaining first level polysilicon coating and thin oxide 34, as well as the field oxide, as a diffusion mask, the slice is now subjected to an N+ diffusion. Phosphorus is deposited and then diffused into the silicon slice 30 to produce all of the N+ regions 11, 12, 13, 14, 32, 33, etc. The depth of diffusion is about 8000 to 10,000 A. The N+ diffused regions function as conductors which connect the various regions together, and also function as the source or drain regions of all the transistors. This diffusion renders highly conductive all of the exposed polysilicon areas such as gates 17 and 21, the strips 18 and 20, the line 29, etc. In the poly-to-moat contact areas N1 and N2, the N+ diffusion penetrates the poly and converts the underlying P-type silicon to N+ because here the oxide layer 34 has been removed. The masks used to define these contact areas when the oxide coating 34 was removed are shown in FIG. 1 as dotted lines 47 and 48. These are much larger than the actual contact areas to allow substantial misalignment.

Oxide is grown over the first level poly by thermal oxidation to produce a layer 49 of about 2000 to 3000 A thickness. At this same time, the exposed silicon in the moat areas is oxidized so the layer 49 extends over the N+ regions 10, 11, 12, 13, 14, 32, 33, etc. If the transistor effect in the resistors R1 and R2 is to be utilized, the oxide layer 49 may be thinner, perhaps 1000 A, although this is at the expense of yield. The oxide may be made thin only under the resistors by growing about 2000 A, patterning the oxide using photoresist to remove that where the resistors R1 and R2 are to be, then growing 1000 A. In this manner the thin oxide area of the chip can be held to a minimum; the total thin oxide area is one of the primary factors influencing yield.

As seen in FIG. 4d, the oxide layer 49 is patterned using photoresist to open the contact areas 25 and 26 and the contact areas at the nodes N1 and N2, that is, all second-poly to first-poly or second-poly-to-moat contact areas.

The second level of polycrystalline silicon is now deposited using a method as for the first level, providing a thickness of about 0.5 micron.

The entire second-level polycrystalline silicon coating is now subjected to a phosphorus implantation which creates the characteristics of the resistors R1 and R2. Areas of polysilicon which are to be highly conductive will be later subjected to a phosphorus diffusion which will leave them heavily doped. To define the resistor characteristics, this implant step is performed at 100 to 150 KeV to a dosage of from 5×10¹³ to 1×10¹⁴ phosphorus atoms per cm², depending upon the desired sheet resistivity for the resistors. Following this phosphorus implant for the resistors, the slices are annealled in an N₂ atmosphere for 30 minutes at 1000° C.; this is for the purpose of distributing the phosphorus properly in the polysilicon.

As reported by Bean et al, Journal of Applied Physics, Vol. 40, No. 5, pp. 2358-2359, April 1969, the resistivity of polycrystalline silicon is 5×10⁵ ohm-cm with an apparent P-type concentration of 2.1×10¹¹ to 5.8×10¹¹ /cm³, and a mobility of 33 to 430 cm² /volt-sec. In polysilicon as the thickness is decreased to less than one micron, the conduction will be along grain boundaries, so resistivity in such case will be at least as high as 10⁵ ohm-cm. The sheet resistance in such case will be [Rs]×[1/d] or 10⁵ ×1(0.5×10⁻⁴) which is approximately 2×10⁸ ohm per square. This would be too unstable with temperature and too highly resistive. The phosphorus implant serves to produce a resistivity of ideally about one to five megohms per square at 25° C. Lower resistivity results in too large cell size, and higher results in instability, nonreproducibility and excessive voltage dependence.

The second level-polysilicon coating is next patterned. This is done by applying a layer of photoresist, exposing to ultraviolet light through a mask prepared for this purpose, developing, then etching with the remaining photoresist masking certain areas of the polysilicon. The resulting structure is seen in FIG. 4e, where a part of the remaining polysilicon layer provides what will be the Vcc line 15 and the extensions 38 and 39 thereof which will have the resistors R1 and R2 and the contacts at the nodes N1 and N2. Also, the discrete areas 40 which reduce the step in a metal-to-moat contact are left in place by this patterning operation. In contrast to the prior application Ser. No. 727,116, no transistor gates are created by this layer of polycrystalline silicon, and indeed it overlies transistor gates.

After patterning the second level polysilicon a protective cap of silicon dioxide is grown on the polysilicon, producing a coating 50 on all exposed surfaces of the poly, including tops and sides. The coating 50 is grown at about 900° C. in steam for about two hours, producing approximately 3000 A thickness and consuming part of the polysilicon. The function of the cap is to prevent deposition of impurities on the resistors or diffusion into the resistors. A photoresist masking and etching operation is then used to remove the coating 50 on all areas of polysilicon except over the resistors R1 and R2. The masks used to define the ocide left to protect the resistor is seen in FIG. 1 defined by dotted lines 51 and 52; these are much wider than the resistors, functioning to permit rather wide margin for error in mask alignment. The masked second-level poly is then subjected to a phosphorus deposition and diffusion, rendering the areas not covered by the oxide 50 highly conductive.

As seen in FIG. 3a, fabrication of the device is continued by depositing a thick layer 37 of phosphorus-doped oxide. Rather than by oxidizing, this is done by a low temperature reaction process using conventional chemical vapor deposition techniques. A layer 37 of about 10,000 A is produced, covering the entire slice. This deposition is followed by a "densification" step wherein the slice is heated at 950° C. for the purpose of eliminating minute holes or pores in the oxide. Subsequently, a photoresist operation opens windows in the oxide layer 37 in areas 25 and 26 where contact is to be made from metal to the second-level polysilicon discrete areas 40 and thus to the moat areas 32 and 33. The step is much less than if the discrete areas 40 were not in place. Although not shown in the FIGURES, at this same time openings are made in the thick oxide 37 were metal to first poly contacts are needed, as in peripheral circuits, though not in the array; for these metal-to-poly contacts a discrete area of second level poly such as the area 40 would also be left in place to reduce the step. Then, a layer of aluminum is deposited on the entire slice, and selectively etched using photoresist masking to produce the desired pattern of metal strips 23 and 24.

In an array of a large number of the cells of FIG. 1, the layout on the chip would make use of considerable economy of space by mirroring the cell about an axis 55 to define the cell on the right of the one shown, and mirroring the cell about the axis 56 to define the cell on the left. The cell is mirrored about an axis 57 to define the cell below it. So, adjacent cells share the Vcc line 15 and the Vss line 12, as well as the mask holes 51 and 52 and edges of the moat areas 10 and 11. The contacts 25 and 26 are staggered and the cell reversed and mirrored about an axis 58, producing the layout of FIG. 5 in an array, so the contact 25 and 26 are shared with the adjacent cell above the axis 58 of FIG. 1. The moats form complex continuous figures shared by entire columns of cells, rather than discrete moat areas. An array of 2¹⁴ or 16384 cells would contain 128 rows and 128 columns of cells, but would require only sixty-four of the N+ diffused moat Vss lines 12 and sixty-four poly Vcc lines 15. 8192 sets of the contacts 25 and 26 would be needed, as they are shared.

It is noted that the process and structure described in this embodiment provides a completely versatile contact and interconnect arrangement. In contrast to prior double-level poly or other like processes, contacts may be made from metal to second poly, metal to first poly, metal to moat (via discrete areas 40 of second poly), second poly to first poly, second poly to moat, or first poly to moat.

Other resistors such as the resistors R1 and R2 can be formed in the first level poly as described in the application Ser. No. 727,116, so resistors would be in both levels. Also, the transistor action of the resistors R1 and R2 would exist in the embodiment where resistors were in the first level poly; the second level poly would then function as the gate.

Although the invention has been described with reference to specific embodiments, this description is not meant to be construed in a limiting sense. Various modifications of the disclosed embodiments, as well as other embodiments of the invention, will become apparent to persons skilled in the art upon reference to the description of the invention. It is therefore contemplated that the appended claims will cover any such modifications or embodiments as fall within the true scope of the invention. 

What is claimed is:
 1. A contact and interconnection arrangement for a semiconductor integrated circuit of the type having circuit elements formed at a face of a semiconductor body, a plurality of levels of contacts and electrode areas and interconnections at said face of the body, the levels including at least one level of polycrystalline silicon and one of metallization on the face as well as elongated regions of monocrystalline semiconductor material in the face, said elongated regions being of opposite conductivity-type and more heavily doped than surrounding material in said face, a first insulating layer on said face between the semiconductor material and said at least one level of polycrystalline silicon and a second insulating layer on said face between said at least one level of polycrystalline silicon and said level of metallization, the improvement wherein: a connection between a contact part of the level of metallization and a contact area on a part of an elongated region of the semiconductor material includes a discrete area of one of the levels of polycrystalline silicon, said discrete area being substantially uniformly doped with impurity between said contact part of the level of metallization and said contact area of said elongated region, said discrete area being solely for the purpose of making electrical connection from said contact part of the level of metallization and said contact area and not being a part of or being connected to said circuit elements except through said contact part of the level of metallization and said contact area on said part of said elongated region of semiconductor material, said discrete area contacting said contact area through a first aperature in said first insulating layer, said first aperature being smaller than said discrete area, said contact part contacting said discrete area through a second aperature in said second insulating layer, said second aperature being smaller than said contact part.
 2. A device according to claim 1 wherein said discrete area is a part of a second level of polycrystalline silicon which at least partially overlies a first level of polycrystalline silicon.
 3. A device according to claim 2 wherein the circuit elements include N-channel silicon-gate MOS transistors and the first level of polycrystalline silicon forms gate electrodes of the MOS transistors.
 4. A device according to claim 3 wherein the second level of polycrystalline silicon extends across parts of the heavily-doped semiconductor material and the first level of polycrystalline silicon does not overly heavily-doped semiconductor material.
 5. A device according to claim 4 wherein a thick insulating coating surrounds the heavily-doped semiconductor material on the face and another thick insulating coating is provided between the second level of polycrystalline silicon and the level of metallization except at said connection.
 6. A contact arrangement for a semiconductor integrated circuit of the type having circuit elements formed at a face of a semiconductor body, at least one of the circuit elements having a region of monocrystalline semiconductor material in the face, said region being of opposite conductivity-type and more heavily doped than surrounding semiconductor material in the face, and a metal strip overlying said face, a part of the metal strip making electrical connection to said region at a contact area, the improvement comprising a layer of polycrystalline semiconductor material directly overlying said region at said contact area and interposed between said part of the metal strip and said region to be included in the electrical connection, said layer being substantially uniformly doped with impurity between said part of the metal strip and said contact area, said layer being solely for the purpose of making electrical connection from said region and not being a portion of any electrical circuit elements, the metal strip not contacting said region except through said layer, a first insulating coating between said face and said layer of polycrystalline semiconductor material with a first aperature in said first coating smaller than said layer, said layer contacting said contact area only through said first aperature, a second insulating coating between said layer and said metal strip with a second aperature in said second coating smaller than said part of the metal strip, said metal strip contacting said layer only through said second aperature. 